Section |
Dimensions |
Mass |
Moment of inertia |
Modulus of Section |
|||
|
Width |
Height |
Thickness |
Per pile |
Wall |
|
|
|
|
w |
h |
t |
|
|
|
|
|
|
mm |
mm |
mm |
kg/m |
kg/m2 |
cm4/m |
cm3/m |
|
|
OZ11AH-775 |
775 |
470 |
5 |
46.7 |
60.3 |
27,838 |
1,180 |
|
OZ13H-775 |
775 |
470 |
5.5 |
51.4 |
66.3 |
30,508 |
1,300 |
|
OZ14H-775 |
775 |
470 |
6 |
56 |
72.3 |
33,158 |
1,410 |
|
OZ15H-775 |
775 |
470 |
6.5 |
60.7 |
78.3 |
35,788 |
1,520 |
|
OZ16H-775 |
775 |
470 |
7 |
65.4 |
84.4 |
38,397 |
1,630 |
|
OZ17H-775 |
775 |
470 |
7.5 |
70.1 |
90.4 |
40,987 |
1,740 |
|
OZ18AH-775 |
775 |
470 |
8 |
74.7 |
96.4 |
43,545 |
1,850 |
|
OZ19AH-775 |
775 |
470 |
8.5 |
79.4 |
102.5 |
46,106 |
1,960 |
|
OZ20AH-775 |
775 |
470 |
9 |
84.1 |
108.5 |
48,635 |
2,070 |
|
OZ21AH-775 |
775 |
470 |
9.5 |
88.7 |
114.5 |
51,145 |
2,180 |
|
OZ22AH-775 |
775 |
470 |
10 |
93.4 |
120.5 |
53,635 |
2,280 |
|
OZ23AH-775 |
775 |
470 |
10.5 |
98.1 |
126.6 |
56,105 |
2,390 |
|
OZ24H-775 |
775 |
470 |
10.75 |
100.4 |
129.6 |
57,332 |
2,440 |
|
OZ08N-800 |
800 |
400 |
5 |
44.4 |
55.4 |
16,611 |
831 |
|
OZ10AN-800 |
800 |
400 |
6.5 |
57.5 |
71.9 |
21,347 |
1,070 |
|
OZ11N-800 |
800 |
400 |
7 |
61.9 |
77.4 |
22,900 |
1,150 |
|
OZ12N-800 |
800 |
400 |
7.5 |
66.4 |
82.9 |
24,442 |
1,230 |
|
OZ13N-800 |
800 |
400 |
8 |
70.8 |
88.5 |
25,971 |
1,300 |
|
OZ14N-800 |
800 |
400 |
8.5 |
75.2 |
94 |
28,001 |
1,400 |
|
OZ14AN-800 |
800 |
400 |
9 |
79.6 |
99.5 |
28,992 |
1,450 |
|
OZ15N-800 |
800 |
400 |
9.5 |
84 |
105.1 |
30,484 |
1,530 |
|
OZ16N-800 |
800 |
400 |
10 |
88.5 |
110.6 |
31,964 |
1,600 |
|
OZ09X-850 |
850 |
405 |
5 |
46.7 |
55 |
18,512 |
910 |
|
OZ10X-850 |
850 |
405 |
5.5 |
51.4 |
60.4 |
20,287 |
1,000 |
|
OZ10AX-850 |
850 |
405 |
6 |
56 |
65.9 |
22,048 |
1,090 |
|
OZ11AX-850 |
850 |
405 |
6.5 |
60.7 |
71.4 |
23,796 |
1,180 |
|
OZ12AX-850 |
850 |
405 |
7 |
65.4 |
76.9 |
25,530 |
1,260 |
|
OZ13AX-850 |
850 |
405 |
7.5 |
70.1 |
82.4 |
27,251 |
1,350 |
|
OZ14X-850 |
850 |
405 |
8 |
74.7 |
87.9 |
28,958 |
1,430 |
|
OZ15X-850 |
850 |
405 |
8.5 |
79.4 |
93.4 |
30,652 |
1,510 |
|
OZ16X-850 |
850 |
405 |
9 |
84.1 |
98.9 |
32,333 |
1,600 |
|
OZ16AX-850 |
850 |
405 |
9.5 |
88.7 |
104.4 |
34,000 |
1,680 |
|
OZ17AX-850 |
850 |
405 |
10 |
93.4 |
109.9 |
35,654 |
1,760 |
|
OZ18X-850 |
850 |
405 |
10.5 |
98.1 |
115.4 |
37,295 |
1,840 |
Malaysia sheet pile heating and air conditioning OZ11AH-775 units should be operating at least five days before OZ13H-775 delivery of the OZ14H-775 floors, during OZ15H-775 installation, and after the OZ16H-775 floors are installed. Cooling to OZ11AH-775 room temperature can be accomplished as quickly as possible, as long as the OZ13AH-775 rate is not so rapid as to cause thermal OZ14H-775 shock. The impact of intensive cereal farming to surface and groundwater in the Orgeval OZ15H-775 watershed was OZ16H-775 assessed by Garnier et al. (2014).
Z type sheet pile OZ 11AH-775 wood is considered OZ 13H-775 acclimated only after OZ 14H-775 reaches EMC for the OZ 15H-775 space in which it is expected OZ 16-775 to perform. Because of its amorphous OZ 11AH-775 molecular configuration, glass reacts to heat OZ 13H-775 differently than do other materials. Several studies go beyond the OZ 14H-775 farm scale, exploring territorial and structural strategies.
Wider boards tend to shrink and swell more than narrower OZ 15H-775 boards because the actual OZ 16H-775 dimension change is proportional to width. Overall, the Seine basin is significantly impacted by agriculture. Glass should be brought down to the anneal-soak temperature as quickly as possible.